Phase Formation and Process Analysis of SiC-Al2O3-Al6Si2O13 Composite Powder via Carbothermal Reduction of Fly Ash at 1 550 ℃

作者：ZHANG Bowen; MA Beiyue; YIN Yue; LI Shiming; ZHANG Zhan; LI Guangqiang; YU Jingkun

来源：China’s Refractories, 2016, 25(04): 33-37.

Silicon carbide(SiC)-alumina(Al2O3)-mullite(Al6Si2O13) composite powder was successfully synthesized at 1 550 ℃ for 5 h via carbothermal reduction reaction,and the effects of various mass ratios of active carbon to fly ash(0.38,0.44 and 0.58) on the phase composition and microstructure of products were investigated,and the formation process of the powder was also analyzed in detail.The products mainly consist ofβ-SiC,α-Al2O3,Al6Si2O13 and FeSi.Increasing carbon content favors the decomposition of Al6Si2O13 and formation of SiC.The average particle size of β-SiC andα-Al2O3 is about 1 μm and that of Al6Si2O13 is 5-10μm.The formation process of SiC-Al2O3-Al6Si2O13powder includes the decomposition of mullite in fly ash and formation of SiC.