Fabrication and performance of a C/C composite using a needled non-woven carbon fiber felt as a preform

作者：Li, Yan; Cui, Hong^*; Zheng, Rui; Ji, A-Lin; Zhou, Shao-Jian

来源：New Carbon Materials, 2017, 32(1): 56-62.

DOI：10.19869/j.ncm.1007-8827.2017.01.001

• Non-woven/felt preform
• Needled C/C composite
• Tensile strength
• Thermal physical properties

A C/C composite was prepared by chemical vapor infiltration followed by repeated pitch impregnation and high pressure carbonization to.a final density of 1.9 g/cm(3) using a needled non-woven carbon fiber felt preform. Its mechanical properties were compared with a 3D woven C/C composite. Results indicated that the axial tensile strength of the needled C/C composite was 24.5 and 52.88 MPa at room temperature and 2800 degrees C, respectively, correspondingly 138 and 170% higher than that of the 3D woven C/C composite. The failure mode of the needled composite was pseudoplastic. The axial thermal expansion coefficient of the needled composite at 1000 degrees C was only 1.409 x 10(-6)/degrees C, 64% lower than that of the 3D woven composite. The needled C/C composite exhibits excellent mechanical strength and thermal physical properties which make it potentially useful for a solid rocket motor.

• 单位
  西北工业大学